Table 8
Examples of interactions in selected fiber matrix system [47].
System | Interaction | Approx. temp. of significant interaction (°C) |
---|---|---|
C–Al | Formation of Al4C3 | 550 |
C(I)–Ni | Fiber recrystallization activated by Ni | 1150–1300 |
C(II)–Ni | Fiber recrystallization activated by Ni | 800 |
B–Al | Formation of bordies | 500 |
SiC–Al | Formation of TiB2 | 750 |
B–Ti | No significant reaction below melting point(Formation of Al4C3) | m.pt 660 |
Sic–Ti | TiSi,Ti5Si3 and TiC form | 700 |
SiC–Ni | Formation of nickel silicides | 800 |
Al2O3–Al | No significant reaction | – |
Al2O3–Ni | Al,O dissolution(very little) gives pits | 1100 |
In air, NiAl2O4 formation | 1100 | |
W–Cu | No interaction upto melting point | m.pt 1083 |
W–Ni | Recrystallization of fiber | 1000 |
Degredation of creep properties | 900 | |
W–Fe | Formation of Fe7W6; dissolution of fiber | 1000 |
Steel-Al | Fe2Al5 formation | 500 |
Tac-Co | Dissolution(dissolution/reprecipitation) | 1200 |
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.