Table 4
Representative summary of the effect of carbon-based additives on mechanical properties.
No. | Bulk Material | Additive percentage |
Mechanical properties measured | Measured value | References |
---|---|---|---|---|---|
1 | Epoxy resin | CNTs 0wt%...... 1wt%......... 2wt%........ 5wt%........ |
Compressive strength (MPa) | ….79.84 ….79.86 ….90.5 ….69.4 |
[81] |
2 | Bamboo/glass fibre hybrid composites. | CNTs 0wt.%........ 0.1wt.%.... 0.3 wt.%.... 0.5 wt.%.... 1.0 wt.%.... |
Tensile strength (MPa) | ….74.038 ….75.318 ….77.540 ….79.763 ….46.797 |
[92] |
3 | Bagasse /glass fiber/cement composites | (MWCNTs) 0wt.%.... 0.5wt.%.... 1wt.%.... 1.5wt.%.... |
Impact strength(J/M2) | ….2400 ….2500 ….2700 ….2600 |
[94] |
4 | Epoxy resin | Carbon black 0wt.%...... 1wt.%...... 2 wt%...... 3wt.%.... 4wt%...... 5 wt. %... |
Flexural strength (MPa) | ….74 ….80 ….84 ….84 ….98 ….70 |
[96] |
5 | Epoxy resin | Graphene oxide 0wt.%...... 1.5wt.%...... 3 wt%...... 4.5wt.%.... 6wt. %... |
Tensile strength (MPa) | ….7 ….13 ….9 ….8 ….7.5 |
[97] |
6 | CNT spun yarns Epoxy resin | long carbon nano-tubes (CNTs) 0%........ Vf of 19.7% … Vf of 19.7% … Vf of 19.7% … Vf of 19.7% … |
Tensile strength (MPa) | ….175 ….212 ….262 ….284 ….467 |
[98] |
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.